Table 2 Tensile strength of PBAT, NCs-PBAT/Cu, NCs-PBAT/Cu|Cu2O, and MCs-PBAT/CuSO4
Sample | At break | |
---|---|---|
Stress (Mpa) | Strain (%) | |
PBAT | 20.43 ± 4.34 | 445.50 ± 53.05 |
NCs-PBAT/Cu 1% | 18.80 ± 5.86 | 414.79 ± 26.63 |
NCs-PBAT/Cu 3% | 21.67 ± 5.25 | 396.96 ± 18.01 |
NCs-PBAT/Cu 5% | 21.57 ± 2.43 | 361.69 ± 39.08 |
NCs-PBAT/Cu|Cu2O 1% | 21.13 ± 5.22 | 423.25 ± 31.51 |
NCs-PBAT/Cu|Cu2O 3% | 20.09 ± 3.48 | 432.07 ± 33.71 |
NCs-PBAT/Cu|Cu2O 5% | 19.38 ± 4.62 | 406.41 ± 46.05 |
NCs-PBAT/CuSO4 1% | 19.70 ± 3.73 | 389.57 ± 61.14 |
NCs-PBAT/CuSO4 3% | 20.69 ± 4.70 | 434.70 ± 29.27 |
NCs-PBAT/CuSO4 5% | 19.38 ± 2.53 | 375.37 ± 22.33 |