Egg Albumin-Assisted Hydrothermal Synthesis of Co3O4 Quasi-Cubes as Superior Electrode Material for Supercapacitors with Excellent Performances


Novel Co3O4 quasi-cubes with layered structure were obtained via two-step synthetic procedures. The precursors were initially prepared via hydrothermal reaction in the presence of egg albumin, and then the precursors were directly annealed at 300 °C in air to be converted into pure Co3O4 powders. It was found that the size and morphology of final Co3O4 products were greatly influenced by the amount of egg albumin and hydrothermal durations, respectively. Such layered Co3O4 cubes possessed a mesoporous nature with a mean pore size of 5.58 nm and total specific surface area of 80.3 m2/g. A three-electrode system and 2 M of KOH aqueous electrolyte were employed to evaluate the electrochemical properties of these Co3O4 cubes. The results indicated that a specific capacitance of 754 F g−1 at 1 A g−1 was achieved. In addition, the Co3O4 cubes-modified electrode exhibited an excellent rate performance of 77% at 10 A g−1 and superior cycling durability with 86.7% capacitance retention during 4000 repeated charge-discharge process at 5 A g−1. Such high electrochemical performances suggest that these mesoporous Co3O4 quasi-cubes can serve as an important electrode material for the next-generation advanced supercapacitors in the future.


With the fast development of science and technology in modern society, relying solely on fossil fuels with limited storage is far from meeting the ever-increasing requirements of energy, so some new energy storage devices with environmental-benign types have been developed rapidly to solve this dilemma [1,2,3]. At present, batteries and supercapacitors are two types of the most promising energy storage systems because of their high performance and low cost. In particular, supercapacitors, also known as electrochemical capacitors, have attracted more attention in terms of their excellence in power density, long-term cycling life, charge-discharge rate, and other properties [4,5,6]. Attributed to such advantages, supercapacitors have been applied in emergency lighting, hybrid electric vehicles, military equipment, and short-term power sources [7, 8]. At the same time, the energy and power density of supercapacitors need to be continuously increased to accommodate the expansion of their application fields; as a result, tremendous efforts have been devoted to resolving this problem. Achieving noteworthy improvements in supercapacitors require a deep fundamental understanding of the charge storage mechanisms. It has been found that the shape, porosity, as well as mechanical properties of electrode materials have a crucial impact on the performances of supercapacitors [9,10,11]. For an ideal electrode material, the number of electrochemically active sites for charge transfer should be enhanced and ionic/electronic transport should be controlled at small diffusion length [12].

Supercapacitors have been differed on the categories on the basis of different energy storage mechanisms. One of them stores energy by charge accumulation at the interface of electrode and electrolyte, and it is known as electric double-layer capacitors (EDLCs). The other is pseudo-capacitors (PCs), which rely on fast Faradic reaction occurring near/on the surface of electrode materials to store energy [13,14,15,16]. The carbonaceous materials, such as activated carbon, graphene, and carbon nanotubes (CNTs) that have large specific surface area and good conductivity, are ideal electrode materials for EDLCs. However, for the carbon-based materials, their inherently low specific capacitance is a sever defect that cannot be ignored, which leads to lower energy density than that of PCs [17]. Conductive polymers as well as metal oxides are commonly used as electrode materials in PCs, due to their favorable pseudocapacitive characteristics of fast and reversible redox reactions. PCs can provide higher energy and power density, larger specific capacitance, and have attracted worldwide research interest [18]. To date, metal oxides, especially transition metal oxides (TMOs), such as MnO2 [19, 20], NiO [21, 22], and Fe2O3 [23, 24], have attracted much attention as potential candidate for electrode materials, for they can provide rich redox charge transfer originated from their variety of oxidation states, which is beneficial to the Faraday reaction. Despite the virtues of low cost and high specific capacitance, the effects of these materials used as electrode in PCs are still not satisfactory, given the fact that they generally possess dramatic volume change, inferior rate-capability, and relatively high resistance; enormous efforts have been devoted to circumvent the hurdles [25]. Among the series of TMOs, Co3O4 is considered as one of the most promising electrode materials. This kind of material possesses a theoretical specific capacitance as high as 3560 F g−1 [26]. Besides, it is environmentally friendly, cheap, and rich in redox activity as well. Unfortunately, compared to its theoretical value, the specific capacitance of Co3O4 electrode achieves in practical applications is significantly low. Ascribed to the limitation transfer of electrons caused by the high internal resistance of Co3O4, only a part of active sites may be involved in the redox reaction, leading to low utilization of the active material and decrease in specific capacitance. Furthermore, the Co3O4 has a dramatic volume change trend during the process of rapid redox reactions, and the collapse of the electrode material leads to a reduction of the cycle life [27].

To address these problems, Co3O4 nanostructures with different morphologies, including nanorods, nanowires, nanoflakes, and nanoflowers, have been successfully prepared by controlling the synthesis process, aiming to increase the surface area and facilitate the redox reaction [28,29,30,31]. The research results have shown that different morphologies have a significant effect on the performance of Co3O4 electrode, but merely changing the morphology is far from being able to improve its inherent poor conductivity and serious volume expansion defects. Researchers are devoted to combine Co3O4 with other highly conductive materials to obtain electrode materials with high charge transfer capabilities. In addition, the synergy between different materials can contribute to the redox reaction at the same time, to achieve the purpose of increasing the specific capacitance [32,33,34,35]. From the point of practical applications and large production, it is significantly important to prepare powder electrode material through a simple synthetic process.

Solution method including hydrothermal/solvothermal route is one of the important synthetic strategies to prepare micro/nanomaterials on a large scale. In this method, surfactant is usually employed to control the rate of nucleation and crystal growth. So the final shape of nanostructures can be effectively tuned by the surfactant [36,37,38]. Several types of surfactant including cationic surfactant, anionic surfactant, nonionic surfactant, and so on can be used for the fabrication of nanomaterials. Among them, the biological molecules with functional groups have received increasing attention due to the environmental-benign of this kind of surfactant. The proteins can interact with inorganic nanoparticles and then to govern the nucleation of inorganic materials in aqueous solutions. Egg albumin, as an important protein, can be widely available from eggs. It has received much attention due to its gelling, foaming, and emulsifying characteristics. In addition, egg albumin is cost-effective and environmentally friendly, and the usage of such surfactant may not result in danger for both environment and the health of humans. Therefore, egg albumin can be employed for the preparation of nanomaterials with controlled morphology. For example, Geng et al. prepared single crystalline Fe3O4 nanotubes with high yields using egg albumin as a nanoreactor [39]. ZnS nanosheets can be synthesized via egg albumin and microwave-assisted method [40]. In addition, dumbbell-shaped BaCO3 superstructures and SnO2 biscuits can be obtained with the assistance of egg albumin by different research group [41, 42]. Overall, the reports on nanomaterials fabrication involving egg albumin have been rarely reported. In this work, porous Co3O4 cubes were synthesized with the assistance of egg albumin via a hydrothermal method and post calcination of the precursors. These Co3O4 porous cubes had average pore size of 5.58 nm, and the Brunauer-Emmett-Teller (BET) specific surface area was evaluated to be 80.3 m2/g. If such Co3O4 cubes were processed into a working electrode, a high capacitance of 754 F g−1 was obtained at 1 A g−1. Besides, if the current density was improved to 10 A g−1, the electrode showed a high rate capability up to 77%. A superior cycling performance with 86.7% capacitance retention (at 5 A g−1) was also achieved during 4000-cycle charge-discharge process. Such excellent electrochemical properties indicate that the porous Co3O4 cubes can serve as a promising electrode material for supercapacitors in the near future.



In this work, all reagents were in analytical pure grade and were used without any additional purification. Urea and cobalt (II) acetate tetrahydrate were purchased from Sinopharm Chemical Reagent Co., Ltd., and egg albumin was obtained from fresh eggs.

Preparation of Porous Co3O4 Cubes

To prepare the porous Co3O4 cubes, 3 mL of egg albumin, 2.4 g of urea, and 0.3 g of cobalt (II) acetate tetrahydrate were dissolved in 37 mL of de-ionized (DI) water with vigorous stirring. Then the mixture was loaded into an autoclave with 50 mL of capacity, and the autoclave was placed in an oven at 140 °C. Five hours later, the precipitates were harvested, rinsed, and dried at 60 °C overnight. The obtained precursor was annealed at 300 °C for 5 h in order that black powder was obtained. Control experiments were conducted with various hydrothermal time (1, 2, 15, and 24 h) and different amount of egg albumin, respectively, while keeping other parameters and procedures the same.

Fabrication of Working Electrode and Electrochemical Tests

On a CHI 660E electrochemical workstation, three kinds of electrochemical tests including cyclic voltammetry (CV), chronopotentiometry (CP), and electrochemical impedance spectroscopy (EIS) were performed based on typical three-electrode configuration, in which platinum wire served as counter electrode and saturated calomel electrode (SCE) was used as reference electrode, respectively. Detailed description about the fabrication of working electrode was as follows: a mixed powder containing active material, acetylene black, and polyvinylidene fluoride (PVDF) with weight ratio of 80:15:5 was prepared firstly, and then the mixed powder was dispersed in N-methyl-2-pyrrolidone (NMP) solvent under ultrasound assistance. The obtained suspension was coated onto pre-cleaned nickel foam (1 × 1 cm2) and vacuum-dried at 85 °C; subsequently, a pressure of 10 MPa supplied by hydraulic press was performed on the nickel foam and the working electrode was finally obtained. All the tests were carried out in 2 M of KOH aqueous electrolyte; the potential of CV tests varied from − 0.1 to 0.65 V, and the scan rates were ranging in 2–50 mV s−1. For the CP tests, the current density differed from 1 to 10 A g−1 with the potential varying from 0 to 0.45 V. An open circuit potential was adopted for the EIS measurement; the frequency region was 10−2–105 Hz and the AC amplitude was 5 mV. The specific capacitance can be obtained from Eq. (1):

$$ {C}_s=\frac{I\cdot \Delta t}{m\cdot \Delta V} $$

where Cs (F g−1) represents the specific capacitance, ∆t (s) indicates discharging time, I (A) is discharging current, ∆V (V) means potential window, and m (g) is the weight of active material.


The X-ray diffraction (XRD) pattern of the sample was collected on a powder X-ray diffractometer (Bruker D8 Advance), in which Cu-kα was used as X-ray source (λ = 0.1548 nm) and the range of 2θ was 25–100°. Field-emission electron microscope (FESEM) images were available from a JEOL JSM7100F scanning electron microscope, and transmission electron microscope (TEM) image was obtained on JEOL JEM2100F equipment with operation voltage of 200 kV. Before TEM measurement, the powder needs to be ultrasonically dispersed in ethanol for 10 min, then is dropped onto a carbon-coated copper grid. Raman examination was performed on RM 1000-Invia (Renishaw) spectrometer, and the wavelength for laser was chosen to be 514 nm. X-ray photoelectron spectroscopy (XPS) measurement was operated on ESCA 2000 spectrometer and Al Kα was employed as excitation source. According to nitrogen adsorption/desorption experiments conducted at 77 K, the Brunauer-Emmet-Teller (BET) surface area was obtained. In addition, pore size distribution (Barrett-Joyner-Halenda, BJH method) could be acquired from the related desorption isotherm.


The shape and size of the sample prepared with 3 mL of egg albumin at 140 °C for 5 h combined with a post annealing process at 300 °C were investigated by SEM (Fig. 1a). It indicated that the product was dominated by a huge amount of cube-like particles with size of about 5–6 μm. The enlarged SEM image (Fig. 1b) demonstrated that some corners for each cube were not perfect, and the cube was assembled with layered structures, as the white arrows pointed. Such novel layered structure could be clearly observed from the SEM image in Fig. 1c. The composition and crystal phase were investigated by XRD technique. Figure 1d displayed the typical XRD pattern, in which all the observed diffraction peaks can be indexed as (111), (220), (400), (422), (511), and (440) crystal planes of cubic Co3O4 (JCPDS No. 43-1003). There were no peaks generated from impurities of Co(OH)2 and CoO, suggesting high purity of the Co3O4 sample obtained herein. The TEM image in Fig. 1e showed an representative Co3O4 cube with size of 5 μm, and the size was in good agreement with the SEM data. Figure 1f exhibited a magnified TEM image that was taken from the position focused on an edge of the cube. The porous structure could be seen, so the total Co3O4 cube was actually composed of many nanoparticle (NP)-based layers. The selected area electron diffraction (SAED) pattern indicated polycrystalline structure, and the spot-based diffraction rings further suggested the large amount of assembled NPs in the porous Co3O4 cube. In addition, the cube was so thick that high-resolution TEM (HRTEM) characterization was difficult to carry out.

Fig. 1
figure 1

a–c SEM images, d XRD pattern, and e, f TEM images of porous Co3O4 quasi-cubes with the SAED pattern in the inset of (f)

The detailed structural information of Co3O4 nanocubes was evaluated by Raman spectrum shown in Fig. 2a. Four characteristic bands located at 468, 509, 611, and 675 cm−1 can be observed, which were corresponding to Eg, \( {\mathrm{F}}_{2\mathrm{g}}^1 \), \( {\mathrm{F}}_{2\mathrm{g}}^2 \), and A1g Raman-active modes, respectively. Such results were in good agreement with previous literatures, further demonstrating the formation of Co3O4 [33, 43]. Figure 2b illustrated a representative full survey XPS spectrum of Co3O4 nanocubes, and no other peaks of impurity can be observed except for the characteristic peaks of carbon, cobalt, and oxygen elements. The full survey XPS data suggested the high purity of the Co3O4 sample. As can be seen from the high resolution of Co 2p spectrum exhibited in Fig. 2c, there are two obvious peaks centered at 779.7 and 794.8 eV, which are corresponding to Co 2p3/2 and Co 2p1/2, respectively. In addition, the energy separation of the two peaks was 15.1 eV, reflecting the existence of Co3+ [14]. Moreover, the two main peaks could be separated into two spin-orbit doublets after Gaussian fitting; the peaks with 779.6 and 794.6 eV binding energies were related to Co3+, whereas others located at 780.9 as well as 796.2 eV were corresponding to Co2+; such observation results matched well with previous report [44]. Two satellite peaks (marked as “sat”) can be observed near the binding energies of 788.6 and 804.1 eV, and their presence further confirmed the characteristic of spinel structures [45]. The fitting results of O 1s spectrum (Fig. 2d) displayed that there were three oxygen contributions (O1, O2, O3). The O1 component located at 529.5 eV can be indexed to typical metal-oxygen bonding, and the O2 component at 531.1 eV is ascribed to the hydroxyl group [46]. As for O3 component with high binding energy of 532.4 eV, it is corresponding to the water molecules absorbed on the electrode surface [47].

Fig. 2
figure 2

a Raman spectrum and b XPS survey spectrum of porous Co3O4 cubes, and the core-level spectra for c Co 2p and d O 1s

The amount of egg albumin in the system played a key role to form such Co3O4 cubes. If no egg albumin was employed, the product was dominated by a lot of Co3O4 nanosheets (Fig. 3a), and the porous structure could be clearly found in the TEM image in Fig. 3b. Such Co3O4 nanosheets were well crystallined; besides, the 0.287 nm of fringe spacing (Fig. 3c) corresponded to the (220) crystal planes of Co3O4. When 0.5 mL of egg albumin was added, the Co3O4 sample was composed of some layered cubes as well as some sheets (Fig. 3d). Co3O4 nanosheets almost completely disappeared as the dosage of egg albumin was increased to 1 mL. Under this condition, Co3O4 qusi-cubes with edge length of about 3–10 μm were formed (Fig. 3e). Uniformed Co3O4 cubes could be obtained as the amount of egg albumin was continuously increased to 3 mL. If we further increased the egg albumin to 5 mL, the morphology of the Co3O4 cubes were well preserved without any change, but the size was reduced to 3–4 μm (Fig. 3f). From the above SEM observations, the formation process of Co3O4 cubes with the assistance of egg albumin can be tentatively proposed. During the reaction, Co2+ ions react with egg albumin to form a complex; the combination of nitrogen-atoms in the egg albumin molecules and Co2+ ions can promote the aggregate growth. Due to the stacking interactions and crystal packing force, the aggregates prefer to grow into flake structure. If the amount of egg albumin is sufficient enough, the flakes tend to be stacked owing to the existence of hydrogen bonds among the molecules, leading to the formation of final layered cube structures.

Fig. 3
figure 3

a SEM image and b, c TEM images of Co3O4 nanosheets obtained without any egg albumin, and the SEM images of the Co3O4 samples prepared with egg albumin of d 0.5, e 1, and f 5 mL

Controlled experiments were also conducted with different hydrothermal reaction time while the dosage of egg albumin was fixed at 3 mL. If the reaction proceeded only 1 h, Co3O4 NPs with irregular shapes were produced in large quantities (Fig. 4a). A small amount of Co3O4 cubes and NPs coexisted when the reaction was extended to 2 h (Fig. 4b). Perfect Co3O4 cubes could be obtained on a large scale as the hydrothermal treatment was prolonged to 5 h; after that, the shape and size almost had no obvious chage with the reaction prolonging to 15 h or longer (Fig. 4c, d). The growth mechanism of Co3O4 cubes and the influence of egg albumin on the final Co3O4 morphology require further detailed investigations, and related research is currently ongoing.

Fig. 4
figure 4

SEM images of the Co3O4 samples synthesized with different hydrothermal durations: a 1, b 2, c 15, and d 24 h

The porosity of these Co3O4 cubes was investigated by nitrogen adsorption-desorption isotherms. The mesoporous structure properties of Co3O4 nanocubes could be clearly revealed by the isotherms shown in Fig. 5a, for such isotherms were categorized as a typical IV type and accompanied with a H3-type hysteresis. The pore size distribution obtained by BJH method further proved this point (Fig. 5b). The average pore diameter of these Co3O4 nanocubes was 5.58 nm, and the BET specific surface area was evaluated to be 80.3 m2 g−1. Especially, it was seen from Fig. 5b that the pore size was dominantly distributed over 4.03 nm. The isotherms of Co3O4 nanosheets was illustrated Fig. 5c, which were similar to the isotherms of nanocubes; however, the BET-specfic surface area of Co3O4 nanosheets was lower than Co3O4 nanocubes, only 52.5 m2 g−1. In addition, the average pore diameter of Co3O4 nanosheets aquaired from Fig. 5d was 4.44 nm. It is well known that electrode materials with large surface area and porosity are more favorable for rapid electrochemical reactions in that the number of electrochemically active sites increases, and the transport of electrons as well as ions accelerates. Attribute to well-distributed pore diameter and large surface area, the Co3O4 nanocubes-modified electrode enable to provide rapid progress of redox reaction and easy penetration of the electrolyte within the electrode, leading to a favorable specific capacitance.

Fig. 5
figure 5

N2 adsorption-desorption isotherms and the corresponding BJH pore size distributions for a, b porous Co3O4 cubes and c, d porous Co3O4 nanosheets, respectively

The electrochemical performance of as-prepared Co3O4 nanocubes was evaluated by CV, CP, and EIS measurements. All the tests were conducted in 2 M of KOH aqueous electrolye using a three-electrode configuration. With the potential varying from − 0.1 to 0.65 V and the scan rate shifting between 2 and 50 mV s−1, the CV curves of Co3O4 nanocubes and nanosheets were presented in Fig. 6a, b, respectively. Both the CV curves had more than one pair of well-defined reduction and oxidation peaks. Such phenomenon implied that the charge storage for Co3O4 nanocubes electrode was governed by pseudocapacitance instead of electrical double-layer capacitance that exhibits rectangular CV curves [48]. Based on the difference in morphology and porosity, the CV curves of the two electrode materials are not completely similar. In terms of the area integrated by CV curves, the Co3O4 nanocubes-modified electrode is significantly larger than the nanosheets-modified electrode, indicating that the Co3O4 nanocubes-modified electrode can deliver higher specific capacitance. As Fig. 6a illustrated that the scan rate accelerated, the two oxidation peaks gradually mingled together to form one broad oxidation peak. In addition, the anodic peaks shifted toward more positive position, whereas the reduction peaks moved to more negative position, suggesting the reversible characteristics of the redox reactions [29]. The pairs of redox peaks on both CV curves were corresponding to the conversion among diverse cobalt oxidation states, and the equations were mainly summarized as follows [49]:

$$ {\mathrm{Co}}_3{\mathrm{O}}_4+{\mathrm{H}}_2\mathrm{O}+{\mathrm{O}\mathrm{H}}^{-}\leftrightarrow 3\mathrm{CoOOH}+{\mathrm{e}}^{-} $$
$$ \mathrm{CoOOH}+{\mathrm{OH}}^{-}\leftrightarrow {\mathrm{CoO}}_2+{\mathrm{H}}_2\mathrm{O}+{\mathrm{e}}^{-} $$
Fig. 6
figure 6

CV curves measured with different scan rates for a porous Co3O4 cubes and b porous Co3O4 nanosheets, CP curves measured with different current densities for c porous Co3O4 cubes and d porous Co3O4 nanosheets, e CP curves of the two electrodes obtained at 1 A g−1, and f specific capacitances obtained at various current densities

The electrochemical capacitive behaviors of the Co3O4 nanomaterials were also investigated by CP tests. Figure 6c, d exhibited the CP curves of Co3O4 nanocubes and nanosheets at various current density, which were acquired over a potential from 0 to 0.45 V. The appearance of distinct potential plateaus in all curves of the two sample demonstrated the pseudocapacitance characteristics, which was consistent with the conclusions obtained from CV curves [50]. According to Eq. (1), the Co3O4 nanocubes-modified electrode delivered specific capacitances of 754, 712, 683, 641, 614, and 581 F g−1, respectively, at the current densities of 1, 2, 3, 5, 7, 10 A g−1. As for the Co3O4 nanosheets-modified electrode, it delivered the specific capacitances of 559, 530, 512, 487, 470, and 452 F g−1 at the same test condition. According to the CP curves of the two kinds of electrodes at 1 A g−1 (Fig. 6e), it is seen that the discharge time of Co3O4 cubes-modified electrode is longer than that of the Co3O4 nanosheets-modified electrode, further demonstrating that the Co3O4 cubes-modified electrode can display superior electrochemical properties. Figure 6f indicates the variation of specific capacitance at different current density for the two kinds of electrodes. Obviously, the specific capacitance reduces gradually as the current density increases. The rate capabilities of the Co3O4 nanocubes and nanosheets-modified electrodes from 1 to 10 A g−1 were 77% and 81%, respectively. It is not difficult to understand that at high current densities, insufficient diffusion of ions and eletrons makes impossible for electrolyte to achieve full contact with the electrode material, resulting in that only the active sites at the outer surface of the electrode material can participate in the redox reaction. Consequently, the incomplete utilization of the active material directly leads to a reduction in specific capacitance. Compared with other previous related literatures, the Co3O4 nanocubes-modified electrode synthesized in this work exhibits superior electrochemical performance (Table 1). It is worth mentioning that the composite electrodes formed by the combination of Co3O4 and other materials tend to exhibit better electrochemical performance. The improved conductivity of composite electrode and the synergy between different substances make a greater contribution to the pesudocapacitance.

Table 1 Comparison for the specific capacitances of Co3O4-based electrode materials

The cycling stability is another vital parameter to measure the appliaction potential of the Co3O4 nanocubes-modified electrode, which is evaluted by 4000 contious CP tests at 5 A g−1. Figure 7 demonstrates that the specific capacitance tends to gradually decrease in the first few hundred cycles, and then stays stable while the cycle number increases; at the end of 4000 cycles, the specific capacitance is 556 F g−1 and remains about 86.7% of the initial value. Such results indicate that the Co3O4 nanocubes-modified electrode possesses excellent long-life cycling durability, which is an important guarantee in supercapacitor applications. The Coulombic efficiency is a parameter that can reflect the reversibility of the redox reaction, which can be calculated by the following equation:

$$ \eta =\frac{t_d}{t_c}\times 100\% $$

where η represents Coulombic efficiency, td and tc indicate discharge and charge time, respectively. The Coulombic efficiency of Co3O4 nanocubes-modified electrode almost remains 100% during the entire cycle test (Fig. 7), and it suggests that the pseudocapacitive reactions are remarkably reversible.

Fig. 7
figure 7

Cyclic stability and Coulombic efficiency of the porous Co3O4 cubes electrodes measured at 5 A g−1

The ion migration and charge transfer characteristics of the Co3O4 nanocubes and nanosheets-modified electrodes were further investigated by EIS measurement and the results were shown in Fig. 8. As we can see that a semicircle in high-frequency region and a straight line in low-frequency region appear in the corresponding Nyquist plot. The internal resistance (Rs) refers to the sum of the ionic internal resistance of electrolyte, the internal resistance of active material, and the contact resistance between electrode material and electrolyte. The Rs value is reflected by the intercept of the semicircle on the real axis (Z’). The resistance of charge transfer reflected by the diameter of the semicircle, the smaller of the diameter, the better transfer of the ions between electrolyte and active material. The Warburg impedance (ZW) can be reflected by the slope of the straight line in low frequency, and ZW is mainly caused by the diffusion of OH ions in electrolyte. In the inset of Fig. 8 is the equivalent circuit fitted from the EIS data, from which a better understanding can be obtained. By analyzing the EIS results of the two electrodes, the Rs were found to be 0.78 and 0.72 Ω for Co3O4 nanocubes and nanosheets-modified electrodes, respectively, which may be attributed to the fact that the thinner sheet-like structure is more favorable for ion permeation in the electrolyte than the cubic structure. Furthermore, the Rct value of the two kind of electrodes were 6.9 and 4.1 Ω, respectively, suggesting that the nanosheets-modified electrode provided higher charge transfer capability.

Fig. 8
figure 8

Nyquist plots of Co3O4 cubes and Co3O4 nanosheets-based electrodes in 2 M KOH solution with the fitted equivalent circuit in the inset


Porous Co3O4 quasi-cubes were prepared through an egg albumin-assisted hydrothermal method with a subsequent high-temperature treatment of precursor in air directly. The size and shape of final Co3O4 samples had a close relationship with the amount of egg albumin and hydrothermal reaction time, respectively. Such Co3O4 cubes possessed a mesoporous characteristic with surface area of 80.3 m2/g, average pore size of 5.58 nm, and main pore size distribution at 4.03 nm. Once these Co3O4 quasi-cubes were processed into a working electrode, it delivered a high specific capacitance of 754 F g−1 at 1 A g−1 and 581 F g−1 at the current density of 10 A g−1. After a continuous 4000 cycles at 5 A g−1, 86.7% capacitance retention could be obtained and it demonstrated a good cycling stability. The outstanding electrochemical properties of these Co3O4 cubes enable them to be promising electrode materials for advanced supercapacitors. In addition, the egg albumin-assisted synthesis route is expected to be extended to prepare other oxides-based electrode materials with novel morphology and superior electrochemical performances.

Availability of Data and Materials

The datasets used and/or analyzed during the current study are obtained from the corresponding author on reasonable request.





Carbon nanotubes



Cs :

Specific capacitance


Cyclic voltammetry


Electric double-layer capacitors


Electrochemical impedance spectroscopy


Field-emission electron microscope








Polyvinylidene fluoride

Rs :

Internal resistance


Selected area electron diffraction


Saturated calomel electrode


Transmission electron microscope


Transition metal oxides


X-ray photoelectron spectroscopy


X-ray diffraction

ZW :

Warburg impedance


  1. Cui L, Huang L, Ji M, Wang Y, Shi H, Zuo Y, Kang S (2016) High-performance MgCo2O4 nanocone arrays grown on three-dimensional nickel foams: preparation and application as binder-free electrode for pseudo-supercapacitor. J Power Sources 333:118–124

    CAS  Article  Google Scholar 

  2. Guan B, Guo D, Hu L, Zhang G, Fu T, Ren W, Li J, Li Q (2014) Facile synthesis of ZnCo2O4 nanowire cluster arrays on Ni foam for high-performance asymmetric supercapacitors. J Mater Chem A 2:16116–16123

    CAS  Article  Google Scholar 

  3. Wang Y, Li S, Sun J, Zhang Y, Chen H, Xu C (2019) Simple solvothermal synthesis of magnesium cobaltite microflowers as a battery grade material with high electrochemical performances. Ceram Int 45:14642–14651

    CAS  Article  Google Scholar 

  4. Feng X, Huang Y, Li C, Xiao Y, Chen X, Gao X, Chen C (2019) Construction of carnations-like Mn3O4@NiCo2O4@NiO hierarchical nanostructures for high-performance supercapacitors. Electrochim Acta 308:142–149

    CAS  Article  Google Scholar 

  5. Feng X, Huang Y, Li C, Chen X, Zhou S, Gao X, Chen C (2019) Controllable synthesis of porous NiCo2O4/NiO/Co3O4 nanoflowers for asymmetric all-solid-state supercapacitors. Chem Eng J 368:51–60

    CAS  Article  Google Scholar 

  6. Han X, Liao F, Zhang Y, Han X, Xu C, Chen H (2019) Solvothermal preparation of zinc cobaltite mesoporous microspheres for high-performance electrochemical supercapacitors. J Alloy Comp 781:425–432

    CAS  Article  Google Scholar 

  7. Yu DY, Zhang ZQ, Meng YN, Teng YF, Wu YP, Zhang XY, Sun QS, Tong WM, Zhao XD, Liu XY (2018) The synthesis of hierarchical ZnCo2O4@MnO2 core-shell nanosheet arrays on Ni foam for high-performance all-solid-state asymmetric supercapacitors. Inorg Chem Front 5:597–604

    CAS  Article  Google Scholar 

  8. Sun J, Li S, Han X, Liao F, Zhang Y, Gao L, Chen H, Xu C (2019) Rapid hydrothermal synthesis of snowflake-like ZnCo2O4/ZnO mesoporous microstructures with excellent electrochemical performances. Ceram Int 45:12243–12250

    CAS  Article  Google Scholar 

  9. Zhou G, Zhu J, Chen YJ, Mei L, Duan XC, Zhang GH, Chen LB, Wang TH, Lu BA (2014) Simple method for the preparation of highly porous ZnCo2O4 nanotubes with enhanced electrochemical property for supercapacitor. Electrochim Acta 123:450–455

    CAS  Article  Google Scholar 

  10. Du W, Liu R, Jiang Y, Lu Q, Fan Y, Gao F (2013) Facile synthesis of hollow Co3O4 boxes for high capacity supercapacitor. J Power Sources 227:101–105

    CAS  Article  Google Scholar 

  11. Krishnan SG, Harilal M, Yar A, Vijayan BL, Dennis JO, Yusoff MM, Jose R (2017) Critical influence of reduced graphene oxide mediated binding of M (M = Mg, Mn) with Co ions, chemical stability and charge storability enhancements of spinal-type hierarchical MCo2O4 nanostructures. Electrochim Acta 243:119–128

    CAS  Article  Google Scholar 

  12. Yu Z, Tetard L, Zhai L, Thomas J (2015) Supercapacitor electrode materials: nanostructures from 0 to 3 dimensions. Energy Environ Sci 8:702–730

    CAS  Article  Google Scholar 

  13. Qiu K, Lu Y, Zhang D, Cheng J, Yan H, Xu J, Liu X, Kim J-K, Luo Y (2015) Mesoporous, hierarchical core/shell structured ZnCo2O4/MnO2 nanocone forests for high-performance supercapacitors. Nano Energy 11:687–696

    CAS  Article  Google Scholar 

  14. Chen H, Wang J, Han X, Liao F, Zhang Y, Gao L, Xu C (2019) Facile synthesis of mesoporous ZnCo2O4 hierarchical microspheres and their excellent supercapacitor performance. Ceram Int 45:8577–8584

    CAS  Article  Google Scholar 

  15. Chen H, Wang J, Han X, Liao F, Zhang Y, Han X, Xu C (2019) Simple growth of mesoporous zinc cobaltite urchin-like microstructures towards high-performance electrochemical capacitors. Ceram Int 45:4059–4066

    CAS  Article  Google Scholar 

  16. Liao F, Han X, Zhang Y, Xu C, Chen H (2018) Solvothermal synthesis of porous MnCo2O4.5 spindle-like microstructures as high-performance electrode materials for supercapacitors. Ceram Int 44:22622–22631

    CAS  Article  Google Scholar 

  17. Lu XH, Yu MH, Wang GM, Tong YX, Li Y (2014) Flexible solid-state supercapacitors: design, fabrication and applications. Energy Environ Sci 7:2160–2181

    Article  Google Scholar 

  18. Hu N, Gong WH, Huang L, Shen PK (2019) Ultrahigh energy density asymmetric electrochemical capacitors based on flower-like ZnO/Co3O4 nanobundle arrays and stereotaxically constricted graphene. J Mater Chem A 7:1273–1280

    CAS  Article  Google Scholar 

  19. Zhang Y, Li GY, Lv Y, Wang LZ, Zhang AQ, Song YH, Huang BL (2011) Electrochemical investigation of MnO2 electrode material for supercapacitors. Int J Hydrog Energy 36:11760–11766

    CAS  Article  Google Scholar 

  20. Liao F, Han X, Cheng D, Zhang Y, Han X, Xu C, Chen H (2019) MnO2 hierarchical microspheres assembled from porous nanoplates for high-performance supercapacitors. Ceram Int 45:1058–1066

    CAS  Article  Google Scholar 

  21. Zhang YQ, Xia XH, Tu JP, Mai YJ, Shi SJ, Wang XL, Gu CD (2012) Self-assembled synthesis of hierarchically porous NiO film and its application for electrochemical capacitors. J Power Sources 199:413–417

    CAS  Article  Google Scholar 

  22. Zhang X, Shi W, Zhu J, Zhao W, Ma J, Mhaisalkar S, Maria TL, Yang Y, Zhang H, Hng HH, Yan Q (2010) Synthesis of porous NiO nanocrystals with controllable surface area and their application as supercapacitor electrodes. Nano Res 3:643–652

    CAS  Article  Google Scholar 

  23. Chaudhari S, Bhattacharjya D, Yu J-S (2013) 1-Dimensional porous α-Fe2O3 nanorods as high performance electrode material for supercapacitors. RSC Adv 3:25120

    CAS  Article  Google Scholar 

  24. Yang S, Song X, Zhang P, Gao L (2015) Heating-rate-induced porous alpha-Fe2O3 with controllable pore size and crystallinity grown on graphene for supercapacitors. ACS Appl. Mater. Inter. 7:75–79

    CAS  Article  Google Scholar 

  25. Bao F, Zhang Z, Liu X, Zhao X (2014) One-step synthesis of hierarchical ZnCo2O4@ZnCo2O4 core–shell nanosheet arrays on nickel foam for electrochemical capacitors. RSC Adv 4:38073–38077

    CAS  Article  Google Scholar 

  26. Yuan C, Yang L, Hou L, Shen L, Zhang X, Lou XW (2012) Growth of ultrathin mesoporous Co3O4 nanosheet arrays on Ni foam for high-performance electrochemical capacitors. Energy Environ Sci 5:7883

    CAS  Article  Google Scholar 

  27. Hao J, Peng S, Li H, Dang S, Qin T, Wen Y, Huang J, Ma F, Gao D, Li F, Cao G (2018) A low crystallinity oxygen-vacancy-rich Co3O4 cathode for high-performance flexible asymmetric supercapacitors. J Mater Chem A 6:16094–16100

    CAS  Article  Google Scholar 

  28. Vijayanand S, Kannan R, Potdar HS, Pillai VK, Joy PA (2013) Porous Co3O4 nanorods as superior electrode material for supercapacitors and rechargeable Li-ion batteries. J Appl Electrochem 43:995–1003

    CAS  Article  Google Scholar 

  29. Gao Y, Chen S, Cao D, Wang G, Yin J (2010) Electrochemical capacitance of Co3O4 nanowire arrays supported on nickel foam. J Power Sources 195:1757–1760

    CAS  Article  Google Scholar 

  30. Xiao A, Zhou S, Zuo C, Zhuan Y, Ding X (2014) Controllable synthesis of mesoporous Co3O4 nanoflake array and its application for supercapacitor. Mater Res Bull 60:674–678

    CAS  Article  Google Scholar 

  31. Che HW, Liu AF (2015) Hierarchical Co3O4 nanoflowers assembled from nanosheets: facile synthesis and their application in supercapacitors. JMater Sci-Mater Electron 26:4097–4104

    CAS  Article  Google Scholar 

  32. Guo D, Zhang M, Chen Z, Liu X-X (2018) The construction of a sandwich structured Co3O4@C@PPy electrode for improving pseudocapacitive storage. RSC Adv 8:33374–33382

    CAS  Article  Google Scholar 

  33. Sun D, He L, Chen R, Lin Z, Lin S, Xiao C, Lin B (2018) The synthesis, characterization and electrochemical performance of hollow sandwich microtubules composed of ultrathin Co3O4 nanosheets and porous carbon using a bio-template. J Mater Chem A 6:18987–18993

    CAS  Article  Google Scholar 

  34. Qiu K, Yan H, Zhang D, Lu Y, Cheng J, Lu M, Wang C, Zhang Y, Liu X, Luo Y (2015) Hierarchical 3D Co3O4@MnO2 core/shell nanoconch arrays on Ni foam for enhanced electrochemical performance. J Solid State Electr 19:391–401

    CAS  Article  Google Scholar 

  35. Liao F, Han X, Zhang Y, Han X, Xu C, Chen H (2019) Hydrothermal synthesis of mesoporous MnCo2O4/CoCo2O4 ellipsoid-like microstructures for high-performance electrochemical supercapacitors. Ceram Int 45:7244–7252

    CAS  Article  Google Scholar 

  36. Fang C, Zhu H, Chen O, Zimmt MB (2018) Reactive two-component monolayers template bottom-up assembly of nanoparticle arrays on HOPG. Chem Commun 54:8056–8059

    CAS  Article  Google Scholar 

  37. Li Z, Fang C, Qian C, Zhou S, Song X, Ling M, Liang C, Liu G (2019) Polyisoprene captured sulfur nanocomposite materials for high-areal-capacity lithium sulfur battery. ACS Appl Polym Mater 1:1965–1970

    CAS  Article  Google Scholar 

  38. Zhao YF, Sun YP, Yin X, Yin GC, Wang XM, Jia FC, Liu B (2018) Effect of surfactants on the microstructures of hierarchical SnO2 blooming nanoflowers and their gas-sensing properties. Nanoscale Res Lett 13:250

  39. Geng B, Zhan F, Jiang H, Guo Y, Xing Z (2008) Egg albumin as a nanoreactor for growing single-crystalline Fe3O4 nanotubes with high yields. Chem Commun 44:5773–5775

  40. Tian X, Wen J, Hu J, Chen Z, Wang S, Peng H, Li J (2016) ZnS nanosheets: egg albumin and microwave-assisted synthesis and optical properties. Solid State Sci 59:39–43

    Article  CAS  Google Scholar 

  41. Ni Y, Li X, Hong J, Ma X (2010) Egg albumin-assisted preparation, characterization and influencing factors of dumbbell-shaped BaCO3 superstructures. Mater Chem Phys 120:10–13

    CAS  Article  Google Scholar 

  42. Tian X, Lian S, Wen J, Chen Z, Wang S, Hu J, Peng H, Peng Y (2017) Egg albumin-assisted sol-gel synthesis and photo-catalytic activity of SnO2 micro/nano-structured biscuits. J Sol-Gel Sci Technol 85:402–412

    Article  CAS  Google Scholar 

  43. Zhang J, Gao W, Dou M, Wang F, Liu J, Li Z, Ji J (2015) Nanorod-constructed porous Co3O4 nanowires: highly sensitive sensors for the detection of hydrazine. Analyst 140:1686–1692

    CAS  Article  Google Scholar 

  44. Wei Y, Ren X, Ma H, Sun X, Zhang Y, Kuang X, Yan T, Ju H, Wu D, Wei Q (2018) CoC2O4 . 2H2O derived Co3O4 nanorods array: a high-efficiency 1D electrocatalyst for alkaline oxygen evolution reaction. Chem Commun 54:1533–1536

    CAS  Article  Google Scholar 

  45. Wu H, Sun W, Shen J, Rooney DW, Wang Z, Sun K (2018) Role of flower-like ultrathin Co3O4 nanosheets in water splitting and non-aqueous Li-O2 batteries. Nanoscale 10:10221–10231

    CAS  Article  Google Scholar 

  46. Chen H, Wang J, Liao F, Han X, Xu C, Zhang Y (2019) Facile synthesis of porous Mn-doped Co3O4 oblique prisms as an electrode material with remarkable pseudocapacitance. Ceram Int 45:8008–8016

    CAS  Article  Google Scholar 

  47. Chen H, Wang J, Liao F, Han X, Zhang Y, Xu C, Gao L (2019) Uniform and porous Mn-doped Co3O4 microspheres: Solvothermal synthesis and their superior supercapacitor performances. Ceram Int 45:11876–11882

    CAS  Article  Google Scholar 

  48. Wang Y, Lei Y, Li J, Gu L, Yuan H, Xiao D (2014) Synthesis of 3D-nanonet hollow structured Co3O4 for high capacity supercapacitor. ACS Appl. Mater. Inter. 6:6739–6747

    CAS  Article  Google Scholar 

  49. Cao Y, Yuan F, Yao M, Bang JH, Lee J-H (2014) A new synthetic route to hollow Co3O4 octahedra for supercapacitor applications. CrystEngComm 16:826–833

    CAS  Article  Google Scholar 

  50. Chen M, Li W, Ma W, Qi P, Yang W, Wang S, Lu Y, Tang Y (2019) Remarkable enhancement of the electrochemical properties of Co3O4 nanowire arrays by in situ surface derivatization of an amorphous phosphate shell. J Mater Chem A 7:1678–1686

    CAS  Article  Google Scholar 

  51. Cui L, Li J, Zhang X-G (2009) Preparation and properties of Co3O4 nanorods as supercapacitor material. J Appl Electrochem 39:1871–1876

    CAS  Article  Google Scholar 

  52. Shim HW, Lim AH, Kim JC, Jang E, Seo SD, Lee GH, Kim TD, Kim DW (2013) Scalable one-pot bacteria-templating synthesis route toward hierarchical, porous-Co3O4 superstructures for supercapacitor electrodes. Sci Rep 3:2325

    Article  Google Scholar 

  53. Zhu Z, Han C, Li T-T, Hu Y, Qian J, Huang S (2018) MOF-templated syntheses of porous Co3O4 hollow spheres and micro-flowers for enhanced performance in supercapacitors. CrystEngComm 20:3812–3816

    CAS  Article  Google Scholar 

  54. Xia X-h, Tu J-p, Mai Y-j, Wang X-l, Gu C-d, Zhao X-b (2011) Self-supported hydrothermal synthesized hollow Co3O4 nanowire arrays with high supercapacitor capacitance. J Mater Chem 21:9319

    CAS  Article  Google Scholar 

  55. Zhou X, Shen X, Xia Z, Zhang Z, Li J, Ma Y, Qu Y (2015) Hollow fluffy Co3O4 cages as efficient electroactive materials for supercapacitors and oxygen evolution reaction. ACS Appl Mater Inter 7:20322–20331

    CAS  Article  Google Scholar 

  56. Fukui K, Suzuki Y (2019) Well-facetted spinel-type Co3O4 microcrystal assembly prepared by hydrothermal synthesis and post-thermal decomposition. Ceram Int 45:9288–9292

    CAS  Article  Google Scholar 

  57. Kong D, Luo J, Wang Y, Ren W, Yu T, Luo Y, Yang Y, Cheng C (2014) Three-dimensional Co3O4@MnO2 hierarchical nanoneedle arrays: morphology control and electrochemical energy storage. Adv Funct Mater 24:3815–3826

    CAS  Article  Google Scholar 

  58. Liu Y, Yu W, Hou L, He G, Zhu Z (2015) Co3O4@highly ordered macroporous carbon derived from a mollusc shell for supercapacitors. RSC Adv 5:75105–75110

    CAS  Article  Google Scholar 

  59. Zhang HN, Chen YJ, Wang WW, Zhang GH, Zhuo M, Zhang HM, Yang T, Li QH, Wang TH (2013) Hierarchical Mo-decorated Co3O4 nanowire arrays on Ni foam substrates for advanced electrochemical capacitors. J Mater Chem A 1:8593–8600

    CAS  Article  Google Scholar 

Download references


The work was supported by the financial supports from International Cooperation of Science and Technology Projects in Shanxi Province (201703D421040 and 201803D421092), and the Scientific Research Foundation for the Returned Overseas Chinese Scholars of Shanxi Province.

Author information

Authors and Affiliations



JLS prepared the materials and the draft of the manuscript. YW, YFZ, and CJX carried out the structure analysis and electrochemical performance test of the samples. CJX and HYC designed the work. HYC approved the manuscript. All authors read and approved the final manuscript.

Corresponding authors

Correspondence to Chunju Xu or Huiyu Chen.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (, which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Sun, J., Wang, Y., Zhang, Y. et al. Egg Albumin-Assisted Hydrothermal Synthesis of Co3O4 Quasi-Cubes as Superior Electrode Material for Supercapacitors with Excellent Performances. Nanoscale Res Lett 14, 340 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:


  • Co3O4
  • Hydrothermal synthesis
  • Electrochemical properties
  • Supercapacitors