Table 1 Summary of the capacitive performance of the supercapacitors based on similar materials

From: Fabrication and Electrochemical Performance of PVA/CNT/PANI Flexible Films as Electrodes for Supercapacitors

Sample

Fabrication method

Ca(mF cm−2)

T

C (%)

Ref

PVA/CNT/PANI film

In situ polymerization

196.5

5000

71.4

Present work

RGO/PPy

In situ reduction polymerization

175

5000

93

[55]

PANI/G paper

Electrochemical polymerization

123

  

[35]

CNT/PANI film

Electrodeposition

184.6

500

95

[56]

PVA/PANI hydrogel

Hydrogel mixing

11.3

  

[33]

CNT/G film

Suction filtration

11

4500

92

[57]

PEDOT/PANI

Acid treatment polymerization

118

5000

82.5

[36]

PVA/CNT@Ni(HCO3)2

Hydrothermal synthesis

143.6

2000

85.5

[58]

PPy/G/Ni-foam

In situ polymerization

165

1500

94.5

[59]

  1. Abbreviations: Ca specifific capacitance; C retention rate of cycle life test; CNT carbon nanotube; G graphene; T cycles of the cycle life test