Table 2 The bandgap changes of scanning speed
From: A Dual Four-Quadrant Photodetector Based on Near-Infrared Enhanced Nanometer Black Silicon
Scanning speed | 0.5 mm/s | 1 mm/s | 5 mm/s | 10 mm/s | Untreaded |
---|---|---|---|---|---|
Bandgap | 1.02 eV | 1.05 eV | 1.08 eV | 1.10 eV | 1.12 eV |