Table 1 List of Raman spectra peak in bulk MoSe\(_{2}\) and WSe\(_{2}\)
From: The Lattice Distortion-Induced Ferromagnetism in the Chemical-Bonded MoSe2/WSe2 at Room Temperature
Material | MoSe\(_{2}\) | MWS | WSe\(_{2}\) | MWS | WSe\(_{2}\) |
---|---|---|---|---|---|
mode | A\(_{{\boldsymbol{1}{\mathrm {g}}}}\) | red shift | A\(_{{\boldsymbol{1}{\mathrm {g}}}}\) | red shift | 2LA(M) |
unit | cm\(^{\boldsymbol{-1}}\) | cm\(^{\boldsymbol{-1}}\) | cm\(^{\boldsymbol{-1}}\) | cm\(^{\boldsymbol{-1}}\) | cm\(^{\boldsymbol{-1}}\) |
800 | 241.6 | 249.4 | X | 254.3 | X |
900 | 241.5 | 249.0 | X | 253.8 | X |
1000 | 241.5 | 249.3 | X | 254.8 | X |
1100-1 | 241.9 | X | X | X | X |
1100-2 | X | X | 250.7 | X | 256.6 |
1100-3 | X | X | 250.7 | X | 256.9 |
1100-4 | X | X | 250.7 | X | 256.3 |
1100-5 | X | X | 250.7 | X | 256.6 |
1100-6 | X | X | 251.0 | X | 256.9 |