Nanoparticles of Block Ionomer Complexes from Double Hydrophilic Poly(acrylic acid)-b-poly(ethylene oxide)-b-poly(acrylic acid) Triblock Copolymer and Oppositely Charged Surfactant

The novel water-dispersible nanoparticles from the double hydrophilic poly(acrylic acid)-b-poly(ethylene oxide)-b-poly(acrylic acid) (PAA-b-PEO-b-PAA) triblock copolymer and oppositely charged surfactant dodecyltrimethyl ammonium bromide (DTAB) were prepared by mixing the individual aqueous solutions. The structure of the nanoparticles was investigated as a function of the degree of neutralization (DN) by turbidimetry, dynamic light scattering (DSL),ζ-potential measurement, and atomic force microscope (AFM). The neutralization of the anionic PAA blocks with cationic DTAB accompanied with the hydrophobic interaction of alkyl tails of DTAB led to formation of core–shell nanoparticles with the core of the DTAB neutralized PAA blocks and the shell of the looped PEO blocks. The water-dispersible nanoparticles with negative ζ-potential were obtained over the DN range from 0.4 to 2.0 and their sizes depended on the DN. The looped PEO blocks hindered the further neutralization of the PAA blocks with cationic DTAB, resulting in existence of some negative charged PAA-b-PEO-b-PAA backbones even when DN > 1.0. The spherical and ellipsoidal nature of these nanoparticles was observed with AFM.

Kabanov and coworkers [12][13][14][15][16][17] first prepared the nanosized BIC using a double hydrophilic poly(ethylene oxide)b-poly(sodium methacrylate) (PEO-b-PMAA) diblock copolymer and various single-, double-and triple-tail cationic surfactants. The micelles or vesicles can be formed depending on length of the PMAA and PEO blocks in PEOb-PMAA and structure of the surfactants. These complexes formed a stable aqueous dispersion and exhibited combined properties of amphiphilic block copolymers and polyelectrolyte-surfactant complexes [12][13][14]. Another type of BIC was formed between cationic PEO-g-poly(ethyleneimine) (PEO-g-PEI) copolymer and anionic alkyl sulfates [18] or sodium salt of oleic acid [19]. The water-dispersible micellelike aggregates with a hydrophobic core of surfactant neutralized PEI chains and a hydrophilic corona of PEO chains were obtained over the whole range of composition. Li and Nakashima [20] prepared the water-dispersible nanoaggregates with the size ranging from 80 to 200 nm from PEO-b-PMAA by binding the cationic surfactant cetyltrimethylammonium chloride (CTAC). They also demonstrated the formation of the PEO-b-PMAA nanoaggregates with the size ranging from 50 to 200 nm through binding with cationic anesthetics [21]. Recently, they fabricated a micelle-like nanoaggregates with the size of 125 to 193 nm using the neutralization of PEO-b-poly(sodium 2-acrylamide-2-methylpropanesulfonate)-b-PAA (PEO-b-PAMPS-b-PAA) triple hydrophilic block copolymer by CTAC [22]. The electrostatic self-assembly of the poly (sodium acrylate)-b-poly(acrylamide) (PANa-b-PAM) diblock copolymer with cationic surfactant dodecyltrimethyl ammonium bromide (DTAB) led to formation of stable 100 nm of colloidal complexes with a core-shell structure. The core was constituted of dense packed DTAB micelles connected by the PANa chains, and the shell formed by PAM chains [23]. Spherical and ellipsoid shaped BIC was also produced by reacting the sodium (sulfamate-carboxylate) isoprene/ethylene oxide (SCIEO) double hydrophilic diblock copolymer with DTAB [24]. In all these cases, the charged head groups of the surfactant were bound to the oppositely charged segments of the polyion blocks, resulting in formation of the hydrophobic core of nanoscale BIC, while the nonionic water-soluble block (e.g., PEO) formed the shell to prevent macroscopic phase separation [12,13]. In contrast to the conventional polyelectrolyte-surfactant complexes, which precipitate from aqueous solution, the BIC are stable and soluble in aqueous dispersion over the entire range of composition, including stoichiometric complexes [12][13][14][15][16][17][18][19][20][21][22][23][24]. Alternatively, the comb-type or random hydrophilic copolymers may be used to produce the watersoluble complex with similar structure of BIC [25][26][27][28][29].
In this work, we tried to fabricate a novel type of waterdispersible BIC using the double hydrophilic poly(acrylic acid)-b-poly(ethylene oxide)-b-poly(acrylic acid) (PAA-b-PEO-b-PAA) triblock copolymer and cationic surfactant DTAB. The BIC formed the core-shell structure nanoparticles with the core consisting of the DTAB neutralized PAA blocks and the thin shell of looped PEO blocks. The looped PEO blocks in the shell hindered the further neutralization of the PAA blocks with cationic DTAB, resulting in that the zeta-potential of the nanoparticles remained negative over the whole DN range. The PAA-b-PEO-b-PAA triblock copolymer with well-defined structure was synthesized via ATRP of tert-butyl acrylate (t-BA) and followed by selective acidolysis of the PtBA block. The nanoparticles of PAA-b-PEO-b-PAA were formed by binding oppositely charged surfactant (DTAB) in aqueous solution has been investigated using turbidimetry, dynamic light scattering (DSL), zeta-potential, and atomic force microscope (AFM).

Synthesis of PAA-b-PEO-b-PAA Triblock Copolymer
The PAA-b-PEO-b-PAA triblock copolymer was synthesized via ATRP of tBA initiated by the Br-PEO-Br macroinitiator and selective acidolysis of the PtBA block. Br-PEO-Br (3.09 g, 0.3 mmol) and Cu(I)Br (0.0864 g, 0.6 mmol) were added in a 50-mL round-bottom flask under argon atmosphere, which was then sealed with a rubber septum. Deoxygenated toluene (8 mL) and tBA monomer (4 mL, 27.6 mmol) were introduced into the flask via an Ar-washed syringe. The mixture was stirred until the Br-PEO-Br macroinitiator was totally dissolved and then three freezing-pump-thaw cycles were performed to remove trace of oxygen in the system. After degassing, 125 lL (0.6 mmol) of PMDETA was injected into the flask using an Ar-washed syringe under continuous stirring until the system became homogeneous. The reaction mixture was stirred at 80°C for 6 h, and then the reaction was terminated by rapid cooling in liquid nitrogen. The crude product was dissolved in THF and passed through a basic alumina column to remove the catalyst, and then precipitated in a large excess of ether. The triblock copolymer PtBA-b-PEO-b-PtBA was obtained by drying in vacuum at room temperature (5.2 g, 79% yield).
Subsequently, hydrolysis was performed by adding excess of trifluoroacetic acid (CF 3 COOH, five-fold molar excess of the t-butyl group) to the PtBA-b-PEO-b-PtBA triblock copolymer solution (2.84 g, C * 150 g/L) in methylene chloride at 0°C under vigorous stirring. The reaction was kept at 0°C for 3 h and then at room temperature for 24 h. The solvent and residual CF 3 COOH were removed by evaporation. The product was washed several times with ether to completely remove trace CF 3 COOH. The PAA-b-PEO-b-PAA block copolymer was filtered and dried in vacuum at room temperature (2.25 g, 98% yield).
The compositions of the PtBA-b-PEO-b-PtBA and PAA-b-PEO-b-PAA triblock copolymers were determined by 1 H NMR spectroscopy using a Bruker Advance Digital 400 MHz NMR spectrometer in CDCl 3 and D 2 O, respectively. The molecular weight M n and molecular weight distribution index M w /M n of PtBA-b-PEO-b-PtBA triblock copolymer were determined with a gel permeation chromatography (GPC, Waters 2410) using THF as the eluent (1.0 mL/min) at 30°C. The calibration curve was established using a set of narrowly distributed PS as the standard. The M n and M w /M n of PAA-b-PEO-b-PAA triblock copolymer were determined with GPC using aqueous solution of 0.1 M Na 2 SO 4 as the eluent (0.6 mL/min) at 25°C. The calibration curve was established using a set of narrowly distributed PEO as the standard. The characterization results of the triblock copolymers are listed in Table 1. The copolymers are referred to as BA 31    diameter D h was determined with the photon correlation spectroscopy using the same instrument at 90°scattering angle. The CONTIN algorithm was adopted in the Laplace inversion of the autocorrelation function to obtain the size distribution of the nanoparticles. D h was evaluated from the Stokes-Einstein equation as R h = kT/3pgD, where k was the Boltzmann constant, T the absolute temperature, g the solution viscosity, and D the apparent diffusion coefficient. The solution was equilibrated for about 5 min before test. An atomic force microscope (AFM, Seiko, SPA 400) was used to observe the nanoparticles in the tapping mode. Mixed solution (5 lL) at DN = 1.0 was dropped on freshly cleaved mica. Water was allowed to evaporate from the grid at atmosphere pressure and 25°C.

Results and Discussions
Solution Behavior of PAA-b-PEO-b-PAA/DTAB Nanoparticles Turbidimetric titration was used to characterize the solubility of the PAA-b-PEO-b-PAA/DTAB nanoparticles prepared at various DN. The turbidity measurement was performed at pH 9.0, at which the ionization of the PAA chains was practically complete. Figure 2 depicts the turbidity of the PAA-b-PEO-b-PAA/DTAB system as a function of DN, the concentrations of the triblock copolymer (C copolymer ) was kept as a constant of 1.0 g/L (C COO À = 0.004 mol/L). No macroscopic phase separation was observed for this system, and the mixed solutions were almost transparent in the whole DN range examined. The results suggest that the PAA-b-PEO-b-PAA/DTAB nanoparticles remain soluble and form stable aqueous dispersions even at the isoelectric point (DN = 1.0). The transparent mixed solutions were obtained in the C copolymer range of 0.1 to 3.0 g/L. As known form the earlier studies by Kabanov and coworkers [12][13][14], the solution behavior of the BIC was strongly dependent on the length of the water-soluble nonionic and ionic blocks. In the present case, the PAA-b-PEOb-PAA triblock copolymer containing a long PEO block (DP = 226) and two short PAA blocks (DP = 31 for each) leads to the excellent solubility for the PAA-b-PEO-b-PAA/ DTAB nanoparticles in water. The nanoparticles are stable and no precipitate was observed after stored for several weeks. The turbidity of the PAA-PEO-PAA/DTAB system at high copolymer concentrations (C copolymer = 10, 20, 50, and 100 g/L) at DN = 1.0 also was measured. The values of turbidity are 0.12, 0.24, 0.53 and 0.67 for the systems at C copolymer = 10, 20, 50, and 100 g/L, respectively. A macroscopic phase separation was observed for the systems of C copolymer = 50 and 100 g/L, and the solution became opalescent at DN = 1.0, indicating precipitation.

Size and f-Potential of the Nanoparticles
The PAA-b-PEO-b-PAA/DTAB nanoparticles were characterized using the DSL and laser microelectrophoresis technique. Figure 3a shows the hydrodynamic diameter (D h ) distribution of the PAA-b-PEO-b-PAA/DTAB particles at various DN with a constant copolymer concentration C copolymer = 1.0 g/L. Only one peak is observed and D h increases with increasing DN, which confirms the formation of the nanoparticles. It should be noted that the concentration of DTAB in our case is much lower than its CMC (20 mM), DTAB should not form micelles itself. gives a negligible effect on the formation and size of the complex. The cationic head groups of the DTAB form salt bonds with the anionic carboxylate groups of the PAA-b-PEO-b-PAA, resulting in the hydrophobic alkyl tails of the DTAB grated to the PAA blocks. This structure is similar to the amphiphilic ABA triblock copolymer composed of long hydrophilic B block and short hydrophobic A blocks [30]. As the nanoparticles are quite stable and the size is close to that of flowerlike micelles formed by amphiphilic  where formation of the PAA-b-PEO-b-PAA/DTAB nanoparticles seems to begin. However, these nanoparticles were unstable and the D h value increase after stored for several days. D h of the nanoparticles is almost constant at 43 ± 3 nm and is unchanged for several weeks when C copolymer ranges from 0.5 to 3.0 g/L. The stable PAA-b-PEO-b-PAA/DTAB nanoparticles were prepared by simply mixing the triblock copolymer with DTAB in aqueous medium in these C copolymer range. At high copolymer concentration (C copolymer range from 10 to 20 g/L), the DLS results revealed that the formation of micelle clusters with larger size of D h = 600-800 nm.
The f-potential of PAA-b-PEO-b-PAA/DTAB nanoparticles as a function of DN is presented in Fig. 5. The absolute f-potential gradually increases from -19.4 to These results are inconsistent with that previously reported complex formed by PEO-b-PMA diblock copolymer with various single-tail cationic surfactants [12][13][14][15]. In those systems, the f-potential approached to zero at DN = 1.0 as the charges of the PMA blocks were neutralized completely. And then it became positive, when DN exceeded 1.0 due to the incorporation of excess surfactants into the complex by hydrophobic interaction between the hydrophobic core of the complex with alkyl chains of surfactants [12][13][14][15]. However, in our PAA-b-PEO-b-PAA/ DTAB system, zero f-potential was not attained when DN [ 1.0, suggesting that the negative charges of the PAA blocks were not neutralized completely. This difference in f-potential seems to be attributed to the difference in the structure of the shell of complexes. In the PEO-b-PMA/ surfactant system, the PEO blocks are grafted on the hydrophobic polyion-surfactant core [12] and extend into the solution to form a loose shell, allowing the excess surfactants to drill through the shell to incorporate with the hydrophobic core. The PEO blocks in the PAA-b-PEO-b-PAA/DTAB system loop to form a dense shell and the looped PEO blocks hinder the further neutralization of PAA blocks, resulting in some non-neutralized negative PAA-b-PEO-b-PAA backbones even when DN [ 1.0. The sizes and f-potential of the PAA-b-PEO-b-PAA/DTAB nanoparticles remain uncharged for several days in the consequent measurements. The morphology of the nanoparticles at different DN has been observed with an AFM. A typical AFM micrograph of the nanoparticles formed by PAA-b-PEO-b-PAA (C copolymer = 1.0 g/L) and DTAB at DN = 1.0 is shown in Fig. 6a. The nanoparticles are in spherical and ellipsoid shapes with diameter from 20 to 40 nm, which agrees well with the DLS results (Fig. 6b).

Conclusions
The novel water-dispersible nanoparticles of double hydrophilic PAA-b-PEO-b-PAA triblock copolymer binding with DTAB were prepared in aqueous solution at pH 9.0 as the result of the neutralization of anionic PAA blocks and cationic DTAB. The spherical and ellipsoid shaped nanoparticles with a core-shell micellar-like structure, in which the core was formed by the DTAB neutralized PAA blocks and the shell was formed by the looped PEO blocks, were formed in the DN range from 0.4 to 2.0. The f-potential of these nanoparticles remained negative over the whole DN range. This is attributed to the structure characters: the looped PEO blocks in the shell of the PAA-b-PEO-b-PAA/DTAB complex hinder the further neutralization of the PAA blocks with cationic DTAB, resulting in existence of some negative charged PAA-b-PEO-b-PAA backbones even when DN [ 1.0. The stable PAA-b-PEO-b-PAA/DTAB nanoparticles with average size of 43 ± 3 nm were prepared by simply mixing the triblock copolymer with DTAB in aqueous medium of C copolymer range from 0.5 to 3.0 g/L at DN = 1.0.