Table 1 Mechanical data of aromatic–aliphatic polyamide/oligomer-MMT hybrid materials
Oligomer-MMT contents (%) | Maximum stress (MPa) ± 0.10 | Maximum strain ± 0.02 | Initial modulus (MPa) ± 0.02 | Toughness (MPa) ± 0.20 | Tg(°C) ± 0.03 | Water absorption at equilibrium (%) |
---|---|---|---|---|---|---|
0.0 | 18.86 | 0.164 | 386.64 | 2.629 | 72.34 | 16.1 |
2.0 | 25.18 | 0.097 | 686.36 | 2.006 | – | 15.5 |
4.0 | 27.58 | 0.090 | 803.02 | 1.986 | 74.57 | 14.8 |
6.0 | 32.12 | 0.073 | 1063.08 | 1.903 | – | 14.2 |
8.0 | 31.77 | 0.072 | 983.74 | 1.753 | 76.09 | 13.3 |
10.0 | 31.10 | 0.062 | 937.24 | 1.445 | – | 12.8 |
12.0 | 30.85 | 0.043 | 891.42 | 0.832 | 81.48 | 12.6 |
14.0 | 28.78 | 0.042 | 889.19 | 0.818 | – | 10.6 |
16.0 | 26.23 | 0.035 | 838.83 | 0.513 | 91.87 | 9.2 |
20.0 | 25.56 | 0.029 | 726.85 | 0.432 | 89.82 | 9.1 |