Table 4 DMTA data of EVA grades and their nanocomposites at 4 wt% filler loading
Sample | Tg (°C) | Storage modulus LogE’ (Pa) at | tan δ at | ||
---|---|---|---|---|---|
T g | 20 °C | T g | 20 °C | ||
EVA40 | −31.6 | 7.93 | 6.18 | 0.76 | 0.13 |
EVA50 | −30.8 | 7.68 | 6.10 | 1.09 | 0.18 |
EVA60 | −26.5 | 6.50 | 5.64 | 1.45 | 0.16 |
EVA70 | −18.5 | 6.03 | 5.27 | 1.51 | 0.21 |
EVA40-4EG | −29.4 | 7.96 | 6.21 | 0.75 | 0.13 |
EVA50-4EG | −28.9 | 7.93 | 6.37 | 0.92 | 0.16 |
EVA60-4EG | −23.5 | 7.40 | 6.24 | 1.24 | 0.22 |
EVA70-4EG | −17.2 | 7.25 | 6.08 | 1.31 | 0.22 |
EVA40-4T | −26.1 | 7.52 | 6.36 | 0.75 | 0.12 |
EVA50-4T | −25.5 | 8.21 | 6.68 | 0.91 | 0.17 |
EVA60-4T | −20.6 | 7.16 | 7.76 | 1.05 | 0.13 |
EVA70-4T | −15.6 | 7.41 | 7.88 | 1.27 | 0.20 |
EVA40-4F | −28.7 | 8.08 | 6.65 | 0.67 | 0.12 |
EVA50-4F | −24.2 | 7.56 | 6.20 | 0.89 | 0.16 |
EVA60-4F | −23.1 | 8.12 | 6.47 | 1.09 | 0.19 |
EVA70-4F | −16.5 | 7.78 | 6.62 | 1.33 | 0.21 |