From: Synthesis and Magnetic Characterization of Metal-filled Double-sided Porous Silicon Samples

Figure 4

Non-saturating term occurring at high magnetic fields above the saturation magnetization of the deposited metal measured on a double-sided sample with two different metals deposited (Ni, Co). The measurements are performed between 4.2 and 310 K with an applied magnetic field perpendicular to the sample surface. A temperature dependence is observed showing a decrease in the magnetization with increasing temperature