Figure 2 | Nanoscale Research Letters

Figure 2

From: Synthesis and magnetic properties of single-crystalline Na2- x Mn8O16 nanorods

Figure 2

SEM and TEM images. (a) Low-magnification SEM image of Na2- x Mn8O16 nanorods; (b) high-magnification SEM image of Na2- x Mn8O16 nanorods; (c) TEM image of Na2- x Mn8O16 nanorods; (d) TEM image of a single Na2- x Mn8O16 nanorod; (e) HRTEM image of the Na2- x Mn8O16 nanorod, the inset of (e) is the corresponding SAED pattern of the nanorod. (f) EDS spectrum of the Na2- x Mn8O16 nanorods. C peak originates from conductive adhesive, Cu peak originates from Cu sheet, and Pt peaks originate from sputtered Pt layer. (a) scale bar 10 μm, (b) scale bar 5 μm, (c) (d) scale bar 500 nm, (e) 5 nm