Table 1 The I-V characterization of TNAs-based DSSCs
Sample | N719ads μmole/cm2 | Film thickness (ηm) | Voc (V) | Jsc (mA/cm2) | FF | η (%) |
---|---|---|---|---|---|---|
TNA | 0.092 | 14 | 0.68 | 3.84 | 0.53 | 1.38 |
TNA-TiCl4 | 0.096 | 15 | 0.66 | 4.83 | 0.51 | 1.61 |
TNA-TnB | 0.116 | 16 | 0.66 | 5.97 | 0.61 | 2.40 |