Figure 2From: Blocking effect of twin boundaries on partial dislocation emission from void surfacesTypical stress-strain curves of the simulated samples. (a) Twin-free Cu samples and (b) NT Cu samples. The diameter d of the central void varies from 2 to 16 nm, while the TB spacing is kept at 25 nm.Back to article page