Table 1 Precipitation polymerization of NIPAM-MBA at 70°C with different MBA amount
MBA (wt%) | D1a(nm) | D2a(nm) | D1/D2 | Particle yield (%) | Soluble polymer (%) | Monomer conversion (%) | Dn(nm) | N p | Observations |
---|---|---|---|---|---|---|---|---|---|
(1014L−1) | |||||||||
2.5 | 1,110 | 498 | 2.23 | 87.14 | 12.35 | 99.49 | 487 | 3.079 | Stable latex |
5.0 | 1,190 | 599 | 1.99 | 90.74 | 8.67 | 99.41 | 564 | 2.064 | White precipitate |
7.5 | 1,004 | 613 | 1.64 | 91.48 | 7.82 | 99.30 | 602 | 1.711 | As above |
10.0 | 1,040 | 716 | 1.45 | 91.78 | 7.06 | 98.84 | 620 | 1.572 | As above |
12.5 | - | - | - | - | - | - | - | - | Coagula |