Table 3 Comparison of SIPPs made with tetradecylamine and a 30-min reflux
Value | Description | Units | TDA-SIPP no. 1 | TDA-SIPP no. 2 |
---|---|---|---|---|
d | Diameter | nm | 7.34 ± 1.22 | 7.86 ± 0.76 |
CV | Coefficient of variation | % | 16.6 | 9.6 |
V p | Particle volume | cm3 | 2.07 × 10−19 | 2.55 × 10−19 |
S | Surface area | cm2 | 1.69 × 10−12 | 1.94 × 10−12 |
C p | Suspension concentration | mg/mL | 4.29 ± 0.47 | 5.97 ± 0.14 |
C Fe | Iron concentration | mg/mL | 0.214 ± 0.00007 | 0.729 ± 0.004 |
C Pt | Platinum concentration | mg/mL | 0.583 ± 0.0003 | 2.503 ± 0.005 |
N a Fe | Iron atoms in 1.0 mL | - | 2.31 × 1018 | 7.87 × 1018 |
N SIPP | Nanoparticles per mL | SIPP/mL | 5.90 × 1014 | 1.83 × 1015 |
A Fe | Atomic percent Fe | at.% | 56.2 | 50.4 |
A Pt | Atomic percent Pt | at.% | 43.8 | 49.6 |
Fe/Pt | Fe/Pt stoichiometry | - | 1.28 | 1.02 |
M P FePt | Mass per particle | g | 2.9 × 10−18 | 3.56 × 10−18 |
N a FePt | Total Fe + Pt atoms per particle | - | 6,964 | 8,551 |
N P Fe | Iron atoms per particle | - | 3913.8 | 4309.9 |
N P Pt | Platinum atoms per particle | - | 3050.3 | 4241.5 |