Figure 1 | Nanoscale Research Letters

Figure 1

From: Ferromagnetism and Ru-Ru distance in SrRuO3 thin film grown on SrTiO3 (111) substrate

Figure 1

HRXRD results for the SrRuO 3 /SrTiO 3 (001) substrate. (a) XRD θ to 2θ scan patterns. The left inset shows the rocking curve of the SrRuO3 (200)c peak. FWHM was as small as 0.057°. The right inset shows good oscillations at low angles due to the uniform thickness of about 38 nm. (b) X-ray reciprocal space mapping around the STO (114) plane showed well-developed peaks for SrRuO3 in the lower region and two strong substrate peaks in the upper region.