Table 1 Molar compositions, synthesis conditions, Si/Al ratio, and particle diameters of zeolite samples
From: Nano- and microsized zeolites as a perspective material for potentiometric biosensors creation
Zeolite type | Composition | Synthesis conditions | Si/Al ratio (crystal)a | Particle size (μm)b |
---|---|---|---|---|
BEA-30 | 1,92Na2O:Al2O3:30SiO2:4,6(TEA)2O:444H2O | 120°C, 7 days | 9.7 ± 1.0 | Approximately 0.4 |
BEA-40 | 1,92Na2O:Al2O3:40SiO2:4,6(TEA)2O:444H2O | 120°C, 7 days | 13.5 ± 1.4 | Approximately 0.4 |
BEA-50 | 1,92Na2O:Al2O3:50SiO2:4,6(TEA)2O:444H2O | 120°C, 7 days | 17.7 ± 1.8 | Approximately 0.4 |
LTA-4 | 1,94Na2O:Al2O3:0,84SiO2:194H2O:1TEA | 100°C, 2 days | 0.84* | 4 |
LTA-9 | 1,94Na2O:Al2O3:0,84SiO2:194H2O:2TEA | 100°C, 3 days | 0.84* | 9 |
LTA-22 | 1,94Na2O:Al2O3:0,84SiO2:194H2O:4TEA | 100°C, 5 days | 0.84* | 22 |