AlGaN/GaN MISHEMTs with AlN gate dielectric grown by thermal ALD technique


Recently, AlN plasma-enhanced atomic layer deposition (ALD) passivation technique had been proposed and investigated for suppressing the dynamic on-resistance degradation behavior of high-electron-mobility transistors (HEMTs). In this paper, a novel gate dielectric and passivation technique for GaN-on-Si AlGaN/GaN metal-insulator-semiconductor high-electron-mobility transistors (MISHEMTs) is presented. This technique features the AlN thin film grown by thermal ALD at 400°C without plasma enhancement. A 10.6-nm AlN thin film was grown upon the surface of the HEMT serving as the gate dielectric under the gate electrode and as the passivation layer in the access region at the same time. The MISHEMTs with thermal ALD AlN exhibit enhanced on/off ratio, reduced channel sheet resistance, reduction of gate leakage by three orders of magnitude at a bias of 4 V, reduced threshold voltage hysteresis of 60 mV, and suppressed current collapse degradation.


AlGaN/GaN-based high-electron-mobility transistors (HEMTs) are capable of delivering excellent performance such as high electron mobility, high saturation current, low on-resistance, and large breakdown voltage, all of which make AlGaN/GaN HEMTs suitable for RF and power applications [1-3]. However, the conventional AlGaN/GaN HEMTs using Schottky gates suffer from low turn-on voltage due to low Schottky barrier between gate metal and AlGaN. On the other hand, the potential of AlGaN/GaN HEMTs is greatly limited for high-speed and high-power applications by the current collapse effect. This effect is also described as dynamic behavior degradation, gate lag, drain lag, etc., which is caused by the charge trapping effect on the AlGaN surface especially in the access region between gate and drain [4-6]. In order to solve these two issues, the deposition of oxide-based dielectric such as SiO2 [7], Al2O3 [8], LaLuO3 [9], and SrO2 [10,11] and dielectric stack such as SiN/Al2O3 [12] as gate dielectric layer and passivation layer in the access region simultaneously is widely adopted. But it has been revealed that the introduction of oxide-based dielectric is likely to form Ga-O bond which is thought as one of interface sources leading to current collapse [13]. In this way, nitride-based dielectrics especially AlN are more favored due to the larger bandgap of AlN compared with that of SiN and smaller lattice mismatch.

Recently, AlN grown by plasma-enhanced atomic layer deposition (PEALD) as passivation layer has been proposed [14,15]. The thickness of AlN can be precisely controlled due to the nature of atomic layer deposition. Meanwhile, in situ surface pretreatment by ammonia (NH3) plasma can significantly suppress the dynamic on-resistance degradation especially under a large drain bias. AlN has also been used as an insertion layer between the Al2O3 and AlGaN to improve the interface [16,17]. However, the possible introduction of damage from plasma treatment may deteriorate the quality of film. Therefore, this work focuses on the thermal ALD AlN passivation method without plasma enhancement. Up to now, there are rare reports on AlN grown by thermal ALD for AlGaN/GaN HEMT passivation [18] and no report on thermal-grown AlN as gate dielectric of GaN HEMTs. The thermal ALD can deposit film with high crystallinity and results in good interface quality due to higher growth temperature. Compared with PEALD AlN using N2 as the source of ammonia in most reported AlGaN/GaN HEMT works, thermal ALD using NH3 instead of N2 can supply N-H more efficiently to remove carbon at the depositing surface [19].

In this letter, we show the thermal ALD AlN film serving as the gate dielectric and passivation technique without the assistance of plasma source. Many advantages such as reduction of gate leakage, improved low threshold voltage hysteresis, and suppressed current collapse degradation are obtained. A breakdown voltage of over 400 V with gate-drain spacing of 10 μm is obtained.


Figure 1a,b shows the schematic cross section of the Schottky gate HEMTs (SGHEMTs) and the AlN HEMTs (AlN-MISHEMTs) with a thermal ALD AlN gate insulator. The measured devices are with a source-gate spacing L GS of 1 μm, gate length L G of 2.5 μm, drain-gate spacing L GD of 6 μm, and gate width of 60 μm.

Figure 1
figure 1

Schematic cross section and dimensions of the HEMTs. (a) Without AlN gate insulator and (b) with AlN gate insulator. These devices are with source-gate spacing L GS of 1 μm, gate length L G of 2.5 μm, drain-gate spacing L GD of 6 μm, and gate width of 60 μm.

In order to study the performance enhancement caused by incorporation of thermal ALD AlN through the comparison between the AlN-MISHEMTs and the SGHEMTs, those devices have an identical layout. The fabrication processes are almost the same except the AlN ALD process step before gate metal deposition. The samples are 2 cm × 2 cm square pieces sliced from the same 6-in GaN-on-Si wafer. The AlGaN/GaN heterostructure on the epi-wafer was grown by metalorganic chemical vapor deposition (MOCVD) on a high-resistivity silicon wafer and consists of 2.5-μm carbon-doped GaN buffer layer, 500-nm i-GaN layer, 1-nm AlN interlayer, 23-nm undoped Al0.25Ga0.75N top barrier layer, and 5-nm GaN cap layer. The sheet carrier density of 9.86 × 1012 cm−2, the two-dimensional electron gas (2DEG) mobility of 906 cm2/Vs, and channel sheet resistance of 700 Ω/sq were obtained by Hall measurement. In the first step, the mesas were defined by BCl3-based reactive-ion etching (RIE). Secondly, ohmic contacts were formed by e-beam evaporation and lift-off of Ti/Al/Ni/Au followed by a rapid thermal annealing at 850°C. The specific contact resistivity and contact resistance were 5.71 × 10−5 Ω · cm2 and 2 Ω · mm, respectively, obtained by transmission line measurement (TLM). Due to the variation of ohmic contact in the fabrication process, the specific contact resistivity and contact resistance of the AlN-MISHEMT sample are 1.81 × 10−5 Ω · cm2 and 1.27 Ω · mm, respectively. The AlN-HEMTs have an AlN gate dielectric layer deposited at a growth temperature of 400°C by using a BENEQ TFS 200 ALD reactor (Beneq Oy, Vantaa, Finland). Before AlN deposition, the surface native oxide was removed by dipping the samples in HCl:H2O (1:10) for 60 s. Trimethylaluminum (TMA) and NH3 have been utilized as aluminum and nitrogen sources, respectively. During all growth experiments, the NH3 gas flow rate was 100 sccm, exposure time was 0.9 s, TMA pulse time was 0.2 s, and purge time in between precursor pulses was 9 s. A total of 100-cycle AlN layers were deposited on the samples. The thickness was about 10.6 nm, measured in the TEM picture in Figure 2. The material composition property of the film is measured by XPS and will be published in the following paper. Atomic concentrations of Al, N, O, and C are 46.8%, 43.2%, 7.4%, and 2.6% respectively. The SGHEMTs omit this AlN thermal ALD step. Finally, Ni/Au gate electrodes were formed by e-beam evaporation and lift-off on both HEMTs.

Figure 2
figure 2

HRTEM cross-sectional view of AlN-MISHEMT.

Results and discussion

Circular Ni-Au/AlGaN-GaN Schottky diode and Ni-Au/AlN/AlGaN-GaN MIS diode are used to characterize the deposited film quality and the interface. Both diodes are with a diameter of 200 μm. The gate leakage current characteristics measured by Agilent 1500 semiconductor analyzer (Keysight Technologies, Inc., Englewood, CO, USA) are shown in Figure 3. With the insertion of thin film AlN gate insulator, the forward current can be reduced by three orders of magnitude at the bias of 4 V and the reverse current can be reduced by about one order of magnitude at the bias of −6 V. A forward gate bias voltage as high as 5.3 V can be reached if the limit of the gate leakage current density is 1 A/cm2.

Figure 3
figure 3

Gate leakage current of Ni-Au/AlGaN-GaN Schottky diode and Ni-Au/AlN/AlGaN-GaN MIS diode.

Agilent 4294 precision impedance analyzer was used to measure the frequency-dependence capacitance-voltage characteristics of the MIS diodes and the Schottky diodes. In Figure 4, the C-V characteristics of the Ni-Au/AlGaN-GaN Schottky diode and the Ni-Au/AlN/AlGaN-GaN MIS diode are compared. A frequency dispersion of about 2.2% in the 2DEG accumulation region can be observed. The threshold voltage dispersion is negligible when the frequency is varied from 1 to 100 kHz. The capacitance of the Schottky and MIS diodes is 272 and 214 nF/cm2, respectively, in the accumulation region.

Figure 4
figure 4

C - V characteristics of Ni-Au/AlGaN-GaN Schottky diode and Ni-Au/AlN/AlGaN-GaN MIS diode.

A comparison of the logarithm scale transfer curves of AlN-MISHEMT and SGHEMT at a drain voltage of 15 V is shown in Figure 5. The threshold voltage and the maximum transconductance G m of AlN-MISHEMT and SGHEMT are −5.7 V and 87 mS/mm and −2.3 V and 70 mS/mm, respectively, determined by linear extrapolation of the transfer curve at the point of peak transconductance. Using AlN as the gate dielectric, AlN-MISHEMT demonstrates a drain current enhancement from 0.396 to 0.563 A/mm at a gate bias of 5 V and a transconductance enhancement from 70 to 87 mS/mm. The channel sheet resistance of AlN-MISHEMT measured from the TLM test structure became 573 Ω/sq, which is smaller than 700 Ω/sq of SGHEMT. That is because of the additional polarization charges caused by AlD AlN film [20]. The transconductance and drain current enhancement might be caused by the reduction of the gate-source and gate-drain series resistance in AlN-MISHEMT. In Figure 5, the off-state drain current of AlN-MISHEMT is also reduced by one order of magnitude at the gate bias of −8 V. Meanwhile, strong reduction in gate leakage current is simultaneously achieved. When these two devices are turned off, the drain leakage current is almost equal to the gate leakage current, which is a clear indication that the off-state drain current is mainly caused by the gate leakage in these devices. Because of the enhanced on-current and reduced leakage current, the on/off ratio is raised from 2.9 to 4.2 decades by using thermal ALD AlN as the gate insulator.

Figure 5
figure 5

Comparison of transfer characteristics of AlN-MISHEMT and SGHEMT with a drain voltage of 15 V.

The transfer and output characteristics of an AlN-MISHEMT are plotted in Figure 6a,b. In the transfer curves shown in Figure 6a, the gate bias is swept forward from −8 to 4 V and swept back from 4 to −8 V with a drain bias of 15 V. A very small threshold voltage hysteresis of 60 mV is observed between these two transfer curves, indicating the good interface between AlN and AlGaN. In Figure 6b, the gate voltage is varied from −6 to 4 V with 2 V/step. The drain current has a maximum drain current of 0.540 A/mm. The drain current may suffer from the electric field-related mobility degradation when the gate voltage is close to 4 V.

Figure 6
figure 6

Transfer and output characteristics of an AlN-MISHEMT. (a) Forward-sweep and back-sweep transfer characteristics of AlN-MISHEMT; (b) output characteristics of AlN-MISHEMT.

To evaluate the degradation of the current collapse in SGHEMT and AlN-MISHEMT, Agilent 1525A signal pulse generator unit was used to perform turn-on pulse-mode measurement. The DC and gate turn-on pulse-mode I DS-V DS characteristics of AlN-MISHEMT and SGHEMT are shown in Figure 7. The gate voltage was pulsed from threshold voltage to 2 V with three different pulse widths of 10, 100, and 500 μs. The drain was pulsed from 0 V to V DS with a pulse width of 9 ms. The total pulse cycle is 10 ms. The current measurement was made at the peak of the gate pulse. As can be seen from Figure 7a, only a slight drain current degradation is observed in the 10-μs pulse measurement for AlN-MISHEMT. Almost no drain current degradation in 100- and 500-μs pulse measurements is observed for AlN-MISHEMT. For comparison, a large drain current collapse can be observed even with 500-μs pulse width in Figure 7b where SGHEMT measurement results are plotted. This comparison suggests that using thermal ALD, AlN can annihilate the surface states and effectively suppress the drain current collapse effect.

Figure 7
figure 7

DC and gate turn-on pulse-mode I DS - V DS characteristics (a) of AlN-MISHEMT and (b) of SGHEMT.

The three-terminal off-state breakdown characteristics of AlN-MISHEMTs with L G = 2.5 μm, L GS = 1 μm, and various L GD were shown in Figure 8. The breakdown voltage is extracted at the point of V DS when the drain current reaches 0.010 A/mm at V GS = −7 V. The inset shows the measured breakdown characteristics of an AlN-MISHEMT with L GD = 10 μm. The breakdown voltage is 280 V with L GD = 6 μm and reaches 425 V with L GD = 10 μm.

Figure 8
figure 8

Relationship between breakdown voltage and gate-drain spacing L GD . Inset: three-terminal off-state breakdown characteristics of an AlN-MISHEMT with L GS = 1 μm, L G = 2.5 μm, and L GD = 10 μm at V GS = −7 V.


The gate dielectric and passivation technique of GaN-HEMT using thermal ALD AlN without plasma enhancement is firstly reported in this letter. The enhanced DC and transient response performances of AlGaN/GaN MISHEMTs with thermal ALD AlN have been comprehensively investigated. With the insertion of thermal AlD AlN, the AlN-MISHEMT delivers a higher I on/I off ratio of 104 due to the reduced gate leakage current of 1 A/cm2 and very small threshold voltage hysteresis of 60 mV, indicating the good interface between AlN and AlGaN. The breakdown voltage of AlN-MISHEMTs is over 400 V with an L GD of 10 μm. The thermal AlD-grown AlN also exhibits effective passivation and improved drain collapse effect. The thermal ALD AlN technique is therefore a very promising method to achieve high-performance GaN MISHEMT for RF and power applications.


  1. Mishra UK, Shen L, Kazior TE, Yi-Feng W. GaN-based RF power devices and amplifiers. Proc IEEE. 2008;96:287–305.

    Article  Google Scholar 

  2. Pengelly RS, Wood SM, Milligan JW, Sheppard ST, Pribble WL. A review of GaN on SiC high electron-mobility power transistors and MMICs. IEEE Trans Microw Theory Tech. 2012;60:1764–83.

    Article  Google Scholar 

  3. Ikeda N, Niiyama Y, Kambayashi H, Sato Y, Nomura T, Kato S, et al. GaN power transistors on Si substrates for switching applications. Proc IEEE. 2010;98:1151–61.

    Article  Google Scholar 

  4. Vetury R, Zhang NQ, Keller S, Mishra UK. The impact of surface states on the DC and RF characteristics of AlGaN/GaN HFETs. IEEE Trans Electron Devices. 2001;48:560–6.

    Article  Google Scholar 

  5. Tirado JM, Sanchez-Rojas JL, Izpura JI. Trapping effects in the transient response of AlGaN/GaN HEMT devices. IEEE Trans Electron Devices. 2007;54:410–7.

    Article  Google Scholar 

  6. Meneghesso G, Verzellesi G, Pierobon R, Rampazzo F, Chini A, Mishra UK, et al. Surface-related drain current dispersion effects in AlGaN-GaN HEMTs. IEEE Trans Electron Devices. 2004;51:1554–61.

    Article  Google Scholar 

  7. Kordoš P, Heidelberger G, Bernát J, Fox A, Marso M, Lüth H. High-power SiO2/AlGaN/GaN metal-oxide-semiconductor heterostructure field-effect transistors. Appl Phys Lett. 2005;87:143501.

  8. Han-Yin L, Bo-Yi C, Wei-Chou H, Ching-Sung L, Jinn-Kong S, Chiu-Sheng H. Enhanced AlGaN/GaN MOS-HEMT performance by using hydrogen peroxide oxidation technique. IEEE Trans Electron Devices. 2013;60:213–20.

    Article  Google Scholar 

  9. Shu Y, Sen H, Hongwei C, Chunhua Z, Qi Z, Schnee M, et al. AlGaN/GaN MISHEMTs with high-κ LaLuO3 gate dielectric. IEEE Electron Device Lett. 2012;33:979–81.

    Article  Google Scholar 

  10. Ye G, Wang H, Arulkumaran S, Ng GI, Hofstetter R, Li Y, et al. Atomic layer deposition of ZrO2 as gate dielectrics for AlGaN/GaN metal-insulator-semiconductor high electron mobility transistors on silicon. Appl Phys Lett. 2013;103:142109–142109-3.

    Article  Google Scholar 

  11. Balachander K, Arulkumaran S, Ishikawa H, Baskar K, Egawa T. Studies on electron beam evaporated ZrO2/AlGaN/GaN metal–oxide–semiconductor high-electron-mobility transistors. Phys Status Solidi A. 2005;202:R16–8.

    Article  Google Scholar 

  12. Anand MJ, Ng GI, Vicknesh S, Arulkumaran S, Ranjan K. Reduction of current collapse in AlGaN/GaN MISHEMT with bilayer SiN/Al2O3 dielectric gate stack. Phys Status Solidi C. 2013;10:1421–5.

    Article  Google Scholar 

  13. Mishra KC, Schmidt PC, Laubach S, Johnson KH. Localization of oxygen donor states in gallium nitride from first-principles calculations. Phys Rev B. 2007;76:9.

    Google Scholar 

  14. Sen H, Qimeng J, Shu Y, Chunhua Z, Chen KJ. Effective passivation of AlGaN/GaN HEMTs by ALD-grown AlN thin film. IEEE Electron Device Lett. 2012;33:516–8.

    Article  Google Scholar 

  15. Chen KJ, Huang S. AlN passivation by plasma-enhanced atomic layer deposition for GaN-based power switches and power amplifiers. Semicond Sci Technol. 2013;28:8.

    Google Scholar 

  16. Shenghou L, Shu Y, Zhikai T, Qimeng J, Cheng L, Maojun W, et al. Performance enhancement of normally-off Al2O3/AlN/GaN MOS-channel-HEMTs with an ALD-grown AlN interfacial layer. In IEEE 26th International Symposium on Power Semiconductor Devices & IC's (ISPSD); 15–19 June 2014. 2014: 362–365.

  17. Ting-En H, Chang EY, Yi-Zuo S, Yueh-Chin L, Huan-Chung W, Shin-Chien L, et al. Gate recessed quasi-normally OFF Al2O3/AlGaN/GaN MIS-HEMT with low threshold voltage hysteresis using PEALD AlN interfacial passivation layer. IEEE Electron Device Lett. 2014;35:732–4.

    Article  Google Scholar 

  18. Koehler AD, Nepal N, Anderson TJ, Tadjer MJ, Hobart KD, Eddy CR, et al. Atomic layer epitaxy AlN for enhanced AlGaN/GaN HEMT passivation. IEEE Electron Device Lett. 2013;34:1115–7.

    Article  Google Scholar 

  19. Kikkawa T, Hosoda T, Akiyama S, Kotani Y, Wakabayashi T, Ogino T, et al. 600 V GaN HEMT on 6-inch Si substrate using Au-free Si-LSI process for power applications. In 2013 1st IEEE Workshop on Wide Bandgap Power Devices and Applications (WiPDA). 2013: 11–14.

  20. Sen H, Qimeng J, Shu Y, Zhikai T, Chen KJ. Mechanism of PEALD-grown AlN passivation for AlGaN/GaN HEMTs: compensation of interface traps by polarization charges. IEEE Electron Device Lett. 2013;34:193–5.

    Article  Google Scholar 

Download references


This work was supported in part by the National Natural Science Foundation of China under Grant 61176074 and Grant 61322404 and in part by the National Science and Technology Major Project of China under Grant 2011ZX02102-003 and Grant 2013ZX02308-004.

Author information

Authors and Affiliations


Corresponding author

Correspondence to Peng-Fei Wang.

Additional information

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

XYL designed and performed the experiments, analyzed the data, and drafted the manuscript. SXZ, LQZ, HFH, JSS, and CMZ participated in the preparation of the devices. HLL, PFW, and DWZ supervised this study. All authors read and approved the final manuscript.

Rights and permissions

Open Access  This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.

The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.

To view a copy of this licence, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Liu, XY., Zhao, SX., Zhang, LQ. et al. AlGaN/GaN MISHEMTs with AlN gate dielectric grown by thermal ALD technique. Nanoscale Res Lett 10, 109 (2015).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:


  • AlGaN/GaN HEMT
  • 2DEG
  • ALD