Fig. 7From: Structural Transformations in Austenitic Stainless Steel Induced by Deuterium Implantation: Irradiation at 295 KTD spectra of deuterium implanted in austenitic steel at radiation doses: (1)—3.5 × 1015 D/cm2; (2)—1.1 × 1016 D/cm2; (3)—3.3 × 1016 D/cm2 Back to article page