Table 1 Mechanical properties of titanium nitride
Consolidation method | T, °C | Density, % | Grain size, nm | Calculated hardness, GPa | HV, GPa | Nanohardness, GPa | E, GPa |
---|---|---|---|---|---|---|---|
MWS | 1400 | 94.5 | 80 | 25 | 20.8 ± 2.4 | 23.09 ± 1.56 | 283 ± 21 |
MWS | 1500 | 96 | 200 | 22 | 21 ± 2.2 | 24.09 ± 1.6 | 301 ± 18 |
PS45 | 1400 | 97.5 | 155 | 23 | 21.9 ± 1.9 | 25.89 ± 3.04 | 314 ± 45 |