Table 1 Relative fraction of sp2, sp3, and C–O components for ta-C films deposited at different biases
From: Endothelialization of TiO2 Nanorods Coated with Ultrathin Amorphous Carbon Films
Bias | Bonds | ||
---|---|---|---|
sp2 C–C (%) | sp3 C–C (%) | C–O (%) | |
C1 (−100 V) | 15.6 | 83.2 | 1.2 |
C2 (−300 V) | 38.3 | 59.4 | 2.3 |
C3 (−900 V) | 58.2 | 30.4 | 11.4 |