Table 3 HDSM fitting results to the experimental values
D (m2 s−1) | k f (m2 s−1) | R 2 | ||
---|---|---|---|---|
SC | 0.1 g | 4.7080e−12 | 9.013e−5 | 0.9542 |
0.25 g | 4.7080e−12 | 4.532e−5 | 0.9927 | |
0.5 g | 4.7080e−12 | 3.015e−3 | 0.9932 | |
DA | 0.1 g | 1.1997e−12 | 2.250e−5 | 0.9624 |
0.25 g | 1.1997e−12 | 1.511e−5 | 0.9924 | |
0.5 g | 1.1997e−12 | 1.125e−5 | 0.9813 | |
AL | 0.1 g | 1.7457e−11 | 5.121e−5 | 0.9997 |
0.25 g | 1.7457e−11 | 3.753e−5 | 0.9988 | |
0.5 g | 1.7457e−11 | 3.254e−5 | 0.9944 | |
MG | 0.1 g | 1.9762e−12 | 3.492e−5 | 0.9981 |
0.25 g | 1.9762e−12 | 2.9178e−5 | 0.9990 | |
0.5 g | 1.9762e−12 | 2.513e−5 | 0.9949 | |
SIL | 0.1 g | 2.6849e−12 | 3.531e−5 | 0.9995 |
0.25 g | 2.6849e−12 | 2.275e−5 | 0.9993 | |
0.5 g | 2.6849e−12 | 1.421e−5 | 0.9978 | |
GCO | 0.1 g | 5.8000e−12 | 4.012e−5 | 0.9978 |
0.25 g | 5.8000e−12 | 3.032e−5 | 0.9979 | |
0.5 g | 5.8000e−12 | 2.051e−5 | 0.9931 | |
PA | 0.1 g | 5.0102e−11 | 3.125e−5 | 0.9995 |
0.25 g | 5.0101e−11 | 2.875e−5 | 0.9986 | |
0.5 g | 5.0101e−11 | 2.523e−5 | 0.9954 |