Table 2 Photovoltaic parameters for the P3HT:PCBM-based PSCs using LiF single and C60 (25 nm)/LiF double CBLs with different thicknesses of LiF
CBL | J sc (mA/cm2) | V oc (V) | FF (%) | PCE (%) | R s (Ω cm2) | R sh (Ω cm2) |
---|---|---|---|---|---|---|
LiF (0.5 nm) | 9.15 | 0.59 | 53.8 | 2.91 | 5.50 | 208.94 |
LiF (1 nm) | 9.21 | 0.58 | 57.2 | 3.06 | 6.14 | 253.56 |
LiF (6 nm) | 7.20 | 0.58 | 18.9 | 0.79 | 195.21 | 62.65 |
LiF (8 nm) | 1.05 | 0.58 | 10.2 | 0.06 | 4749.92 | 175.15 |
C60/LiF (0.5 nm) | 10.03 | 0.59 | 60.2 | 3.57 | 4.95 | 323.33 |
C60/LiF (1 nm) | 10.10 | 0.56 | 66.6 | 3.77 | 5.05 | 626.63 |
C60/LiF (6 nm) | 8.21 | 0.54 | 59.8 | 2.65 | 8.98 | 744.54 |
C60/LiF (8 nm) | 6.96 | 0.54 | 29.2 | 1.10 | 14.08 | 82.15 |