Fig. 36
From: Research Progress in Rare Earth-Doped Perovskite Manganite Oxide Nanostructures
a–c Temperature dependent|∆SM| at different magnetic field calculated from M–H data for the SSMO/STO, SSMO/LSAT, and SSMO/LAO films, respectively. Inset of (b) and its inset shows the one cycle M–H curves of the SSMO/LSAT film in the temperature interval of 2 K and 1 K, respectively. Inset of (c) shows one cycle M–H curves of the SSMO/LAO films in the temperature interval of 5 K. d CP(T) of the SSMO/LAO film at μ0H = 0 T. e The ∆SM vs. T curve of the SSMO/STO film at μ0H = 6 T. The bigger rectangular sketch and shaded area corresponds to RCP-1 and RCP-2, respectively. Inset shows the value of RCP-2 as a function of magnetic field for three different films. f The value of RCP-1 as a function of magnetic field for three different films. Sm0.55Sr0.45MnO3 (SSMO) thin films deposited on LaAlO3 (LAO), SrTiO3 (STO), and (La0.18Sr0.82)(Al0.59Ta0.41)O3 (LSAT) single crystalline substrates are named as SSMO/STO, SSMO/LSAT, and SSMO/LAO, respectively. Reproduced with permission of [235]