Table 3 E, σm, εm, and σf of samples under tension along x- or y-direction at a strain rate of 5 × 108 s−1

From: Effects of Anisotropy and In-Plane Grain Boundary in Cu/Pd Multilayered Films with Cube-on-Cube and Twinned Interface

  Loading direction E (GPa) σm (GPa) εm σf (GPa)
SC COC x \([01\overline{1}]\) 135.04 7.93 0.063 3.500.08
SC Twin x \([01\overline{1}]\) 133.84 7.66 0.061 3.110.07
SC COC y \([\overline{2}11]\) 145.62 12.39 0.093 4.760.07
SC Twin y \([\overline{2}11]\) 142.95 12.42 0.095 5.500.12
HC COC x 137.38 6.27 0.056 4.920.16
HC Twin 136.08 6.66 0.065 5.550.08